P. Li, D. Ellsworth, H. Chang, P. Janantha, D. Richardson, et al. Generation of Pure Spin Currents via Light-Induced Spin Seebeck Effect in Self-Biased Hexagonal Ferrite Films
点击次数：
DOI码：10.1063/1.4904479
发表刊物：Appl. Phys. Lett.
摘要：Light-induced generation of pure spin currents in a Pt(2.5 nm)/BaFe12O19(1.2 μm)/sapphire(0.5 mm) structure is reported. The BaFe12O19 film had strong in-plane uniaxial anisotropy and was therefore self-biased. Upon exposure to light, a temperature difference (ΔT) was established across the BaFe12O19 thickness that gave rise to a pure spin current in the Pt via the spin Seebeck effect. Via the inverse spin Hall effect, the spin current produced an electric voltage across one of the Pt lateral dimensions. The voltage varied with time in the same manner as ΔT and flipped its sign when the magnetization in BaFe12O19 was reversed. This work was supported in part by the U.S. Army Research Office under Award # W911NF-14-1-0501; the U.S. National Science Foundation under Award # ECCS-1231598; C-SPIN, which is one of the SRC STARnet Centers sponsored by MARCO and DARPA; and SHINES, which is an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science, Basic Energy Sciences under Award # SC0012670. Mr. Himadri Dey, Professor Gyorgy Csaba, and Professor Wolfgang Porod are gratefully acknowledged for helping cut substrates.
论文编号：242412
学科门类：工学
卷号：105
期号：24
是否译文：否
发表时间：2014-11-09
上一条：P. Li, V. Sankara, F. Shah, H. Dey, G. Csaba, et al. Fabrication of Pseudo-Spin-Valve Giant Magnetoresistance Arrays for Nanomagnet Logic by Liftoff and the Snow-Jet Process.
下一条：P. Li, G. Csaba, M. Niemier, X. S. Hu, J. Nahas, et al. Power Reduction in Nanomagnet Logic using High-Permeability Dielectrics.